Fe/Tb multilayers with various Fe layer thickness and fixed Tb layer thickness wereprepared by e-beam alternate vapor deposition. Analyses of the microstructure of thesefilms show that the magnetic performance is strongly affected by the interface struc-ture. Fe in the films evolved to amorphous phase and the Fe/Tb interface becameindiscernible with decreasing Fe thickness. At the same time, the film was observedto perform superparamagnetically, which is quite different from the ferromagnetic be-havior of Fe/Tb multilayers that have sharp Fe/Tb interface. Our work shows thatthe interface roughness has strong influence to the properties of magnetic multilayers.
关键词:
magnetic multilayer
,
null
祁先进
,
李国华
,
王寅岗
,
李子全
功能材料
采用高真空直流磁控溅射的方法制备了结构为//Ta(5nm)/Co_(75)Fe_(25)(5nm)/Ir_(20)Mn_(80)(12nm)/Ta(8nm)的双层膜,通过X射线衍射(XRD)、原子力显微镜(AFM) 和振动样品磁强计(VSM)研究了退火对双层膜的结构及磁性能的影响;并通过样品在反向饱和场下停留不同的时间,研究了退火对双层膜的磁稳定性的影响.结果表明,退火使得IrMn(111)织构减弱,表面/界面粗糙度增大,交换偏置场减小,矫顽力增加,退火降低了双层膜的磁稳定性.
关键词:
退火
,
织构
,
界面粗糙度
,
交换偏置场
杨素分
,
陈冷
功能材料
doi:10.3969/j.issn.1001-9731.2016.07.012
用X射线衍射仪、原子力显微镜和磁强计研究了Ta缓冲层厚度变化时,Ta/FeMn/NiFe/Ta多层膜微观结构和磁性能的变化,分析了其微观结构和磁性能之间的关系。实验结果表明,随 Ta 缓冲层厚度增加,FeMn层织构、晶粒尺寸、位错密度、应变和界面粗糙度都发生明显变化,并且这些变化影响了多层膜的偏置场(H ex )和矫顽力(H c )的大小。结合实验现象和交换偏置(EB)的物理本质,讨论了微观结构对交换偏置的影响机理。
关键词:
交换偏置
,
多层膜
,
织构
,
界面粗糙度
,
晶粒尺寸
王帅创
,
梁新刚
工程热物理学报
通过求解声子辐射输运方程(EPRT)计算得到了薄膜的面向晶格热导率.在薄膜界面采用与声子波长相关的镜反射率模型,考虑了薄膜的厚度、温度和表面粗糙度等对其热导率的影响.结果表明,界面粗糙度对薄膜热导率的影响很大.减小界面粗糙度,会使得薄膜热导率大大增加.另外,薄膜厚度减小使得热导率峰值对应的温度增加.
关键词:
热导率
,
薄膜
,
表面粗糙度